阿拉丁的 30 NR-D 透明二氧化钛浆料采用 43T 丝网印刷时可产生 6-7μm 的烧结膜厚度。阿拉丁的 30 NR-D 透明二氧化钛浆料具有高度分散且稳定的锐钛矿纳米颗粒。它针对使用合成 43T 网筛（或类似物）的丝网印刷进行了优化。干燥后，这种糊状物必须在 500°C 或以上进行烧制。这会产生透明的烧结层，当使用 43T 网筛时，一层印刷层的薄膜厚度约为 6-7μm，两层印刷层的薄膜厚度约为 12μm。 该浆料具有最佳的流变性能，可提供良好的表面均匀性，并含有专门配制的有机粘合剂，可提供适用于各种染料/电解质系统的多功能孔隙率。 Aladdin's 30 NR-D transparent titanium dioxide slurry can produce 6-7 μ M of the thickness of the sintered film. Aladdin's 30 NR-D transparent titanium dioxide slurry has highly dispersed and stable anatase nanoparticles. It is optimized for screen printing using synthetic 43T screen (or similar). After drying, the paste must be fired at 500 ° C or above. This will produce a transparent sintered layer. When 43T screen is used, the film thickness of one printed layer is about 6-7 μ m. The film thickness of two printing layers is about 12 μ m。 The slurry has the best rheological properties, can provide good surface uniformity, and contains specially prepared organic adhesives, which can provide multi-functional porosity for various dye/electrolyte systems. Aspect ：Off white paste Average Nanoparticle Size (active) 30nm Suggested Mesh Screen 43T Sintered Layer 5-6μm transparent
All
Chemical Reagents
Biomedicine
Organic raw materials
Inorganic chemical industry
intermediate
Agricultural chemicals
Auxiliaries and catalysts
Fragrances and Flavors
Dyes and Pigments
Daily chemical industry
30 NR-D Titania Paste
CAS number：unknown molecular formula：
overview
compound introduction
Specs
| Chinese alias | - | ||
| English alias | - | ||
| CAS number | unknown | molecular formula | |
| molecular weight | - | Exact mass | - |
| PSA | - | logp | - |
numbering system
No numbering system information yet
physicochemical properties
No physical and chemical property information yet
Safety information
No safety information yet
Production methods and uses
No production method and use information yet
Related
upstream information
No upstream information yet
downstream information
No downstream information yet
MSDS
Found 0 shareMSDS